| Melt Index, g/10min (Condition 190/2.16) | 2.5 | |
| Density, g/cm3 | 0.921 | |
| Vicat Softening Temperature, oC (oF) | 95 (203) | |
| BLOWN POLY FILM PROPERTIES | ||
| Haze, % | 5.5 | |
| Gloss @ 45o, Gardner Rating | 68 | |
| Transparency, % | 30 | |
| Elmendorf Tear Strength, g |
M.D |
320 |
| |
T.D |
170 |
| Tensile Strength @ Yield, MPa (psi) |
M.D |
23 (3,400) |
| |
T.D |
10 (1,500) |
| Tensile Strength @ Break, MPa (psi) |
M.D. |
23 (3,400) |
| |
T.D |
18 (2,600) |
| Tensile Modulus of Elasticity, MPa (psi) |
M.D |
172 (25,000) |
| T.D |
193 (28,000) | |
| Dart Impact, g | 75 | |
| Elongation @ Break % |
M.D. |
300 |
| |
T.D. |
550 |
| Coefficient of Friction | 0.15 | |
| Water Vapor Transmission Rate, g/m2*24h (g/100 in.2*24h) |
18.6 (1.2) | |
| O2 Permeability, cm3*mm/m2*24h*atm (cm3*mil/100 in.2*24h*atm) |
200 (506) |