| POLY PROPERTIES |
ASTM |
UNITS |
TYPICAL VALUES |
|
| Melt Index |
D1238 | g/10min | 1.0 | |
| Density | D792 | g/cm3 | 0.918 | |
| POLY FILM PROPERTIES |
||||
| Thickness | um (mil) |
25 (1.0) |
||
| Tear Strength |
MD |
D1922 | g | 100 |
| TD | g | 330 | ||
| Dart Drop Impact, F50 |
D1709/A | g | 100 | |
| Low Friction |
J/mm (in-lb/mil) |
34 (8) |
||
| Tensile Strength |
MD | D882 | MPa (psi) |
49 (7,100) |
| TD | MPa (psi) | 34 (4,900) |
||
| Yield Strength |
MD | D882 | MPa (psi) | 11 (1,600) |
| TD |
MPa (psi) | 11 (1,600) |
||
| Elongation | MD | D882 | % | 540 |
| TD | % | 830 | ||
| 1% Secant Modulus |
MD | D882 | MPa (psi) | 200 (28,000) |
| TD | MPa (psi) | 230 (33,000) |
||
| Haze | D1003 | % | 11 | |
| Gloss @ 45o |
D2457 | 56 |